Acrypet三菱麗陽PMMA V 001物性表（中英文版）
|
MITSUBISHI RAYON Acrypet® V 001 PMMA
|
||
|
特性用途：適合于擠出成型板，普通擠出板。
|
||
|
Physical Properties物理性質
|
Metric公制數據
|
Comments測試方法
|
|
Specific Gravity密度
|
1.19 g/cc
|
JIS K7112;ISO 1183
|
|
Water Absorption吸水率
|
0.3 %
|
24 hours; JIS K7209; ISO 62
|
|
Mold Shrinkage成型收縮率
|
0.2-0.6%
|
MRC Method
|
|
Melt Index of Compound熔體流動速率
|
JIS K7210；ISO 1133
|
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
Comments測試方法
|
|
M scale洛式硬度M
|
95
|
JIS K7202；ISO 2039
|
|
Tensile Strength at Break抗拉強度
|
75.0 MPa
|
JIS K7162; ISO 527
|
|
Elongation at Break斷裂伸長率
|
7 %
|
JIS K7162; ISO 527
|
|
Flexural Strength抗彎強度
|
135.0 MPa
|
JIS K7171; ISO 178
|
|
Flexural Modulus彎曲彈性模量
|
3.30 GPa
|
JIS K7162; ISO 527
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度
|
1.40 kJ/m2
|
JIS K7111; ISO 179
|
|
Electrical Properties電性能
|
Metric公制數據
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
>1013Ωm
|
JIS K6911
|
|
Dielectric Constant介電常數
|
3.7
@Frequency 60 Hz |
JIS K6911
|
|
Dielectric Strength絕緣擊穿強度
|
20.0 MV/m
|
4kV/s; JIS K6911
|
|
Dissipation Factor介質衰耗因數
|
0.05
@Frequency 60 Hz |
JIS K6911
|
|
Thermal Properties熱性能
|
Metric公制數據
|
Comments測試方法
|
|
CTE, linear線性膨脹系數
|
6×10-5 1/℃
|
JIS K7197
|
|
Deflection Temperature at載荷撓曲溫度1.8 MPa (264 psi)
|
93.0 °C
|
JIS K7191；ISO 75
|
|
Vicat Softening Point維卡軟化點
|
100 °C
|
B50; JIS K7206；ISO 306
|
|
Annealing Point退火點(空氣浴)
|
85.0 - 90.0 °C
|
1-3 hours
|
|
Flammability, UL94阻燃等級(1.5mm,3.0mm)
|
HB
|
File No.E256044
|
|
Optical Properties光學性質
|
Metric公制數據
|
Comments測試方法
|
|
ReFRactive Index折射率
|
1.49
|
JIS K7142/ISO 489
|
|
Haze霧度
|
0.3 %
@Thickness 3.00 mm |
JIS K7136/ISO 14782
|
|
TRansmission, Visible光線透射率
|
93 %
@Thickness 3.00 mm |
JIS K7361/ISO 13468
|
|
Processing Properties加工性能
|
Metric公制數據
|
Comments測試方法
|
|
Processing Temperature加工溫度
|
200 - 260 °C
|
Injection molding cylinder temperature
|
|
Mold Temperature模具溫度
|
40.0 - 80.0 °C
|
|
|
Drying Temperature干燥溫度
|
70.0 - 80.0 °C
|
|
|
Dry Time干燥時間
|
4 - 6 hour
|
|
|
Injection Pressure注射壓力
|
70- 150 MPa
|
|
|
螺桿L/D
|
25～36
|
|
|
Front Barrel Temperature料筒前段溫度
|
190～220℃
|
|
|
Middle Barrel Temperature料筒中段溫度
|
210～230℃
|
|
|
Rear Barrel Temperature料筒后段溫度
|
210～230℃
|
|
|
Die Temperature模頭溫度
|
210～230℃
|
|
Acrypet三菱麗陽PMMA V 001物性特性用途
PMMA V 001特性用途：適合于擠出成型板，普通擠出板。
PMMA V 001原產地及生產廠商：三菱麗陽高分子材料（南通）有限公司/日本三菱麗陽株式會社MITSUBISHI RAYON CO.,LTD.
PMMA V 001產品產生氣泡的原因及解決辦法
這是發生在產品壁厚的地方的空洞。若是透明產品、會成為以后無法彌補的外觀缺陷。事先干燥不充分或者料筒溫度過高會在壁厚中心部分以外的地方發生氣泡。收縮現象集中于壁厚的地方會在壁厚中心部分型成氣泡。可以通過防止收縮現象發生的方法來防止、也可通過以下辦法解決：
1，脫離模具后用水冷卻時、增加水的溫度或縮短用水冷卻的時間
2，提高模具溫度